Made of good quality phlogopite mica, after chemical or mechanical processing, reinforced with fiberglass cloth or stainless steel tanged sheet.
Hp5 Series Rigid mica sheets for heat equipment is a kind of plate like insulating materials made of muscovite paper or phlogopite paper mixed with Silicone bonded after pressed and baked It has good mechanical strength and property of heat resistance , It can be used with 550-800for a long time ,It has been widely used in metallurgy, chemical and electric industries, etc. The products are certified by UL and in conformity with IEC.
Application
Specially suit for high temperatures and aggressive acids.
Mica roll can be cut into mica filler of spiral wound gasket.
Specification
|
Item |
Phlogopite Mica Roll |
Mica Roll W /Glassfiber Cloth |
Mica sheet W /SS316,304 Tanged Insert |
|
Density DIN37754(g/cm3) |
1.9 |
1.9 |
2.1 |
|
Max temperature (℃) |
1000 |
1000 |
1000 |
|
Compressibility ASTM F 36A(%) |
20~25 |
18~23 |
10~15 |
|
Recovery ASTM F 36A(%) |
45~50 |
45~50 |
50~55 |
|
Tensile strength ASTM F152（Mpa） |
15 |
20 |
25 |
|
Max .gasket to load （Mpa） |
45 |
60 |
100 |
|
Sealability for nitrogen at 30 Mpa and 6 bar,temperature within 100to 400℃ Max(ml/min) |
0.3 |
0.4 |
0.2 |
|
Thickness increase ASTM F 146 oill JRM 903:5H/150℃(%) |
15 |
15 |
12 |
|
Weight increase ASTM F 146 oill JRM 903:5H/150℃(%) |
30 |
28 |
26 |
|
Ignition loss DIN52911(%) |
＜10 |
＜10 |
＜5 |
|
Stress relaxation DIN 52913 50Mpa,16h/300℃(Mpa) |
30 |
35 |
40 |
|
Item |
Thickness (mm) |
Width （mm） |
Length (mm) |
|
Phlogopite mica roll SG-S36011 |
0.2~2 |
≤1000 |
≤50000 |
|
Mica roll with glassfiber cloth SG-S36012 |
0.2~2 |
≤1000 |
≤50000 |
|
Mica sheet with SS316 And SS304 tanged insert SG-S36013 |
1~3 |
≤1000 |
≤1200 |
Feature
1. High-temperature insulation
2. High dielectric strength
3. Good resistance to high heat and high voltage
4. Excellent mechanical strength